ABS:耐劃傷性材料,用于平板電視的表面材料;韓國三星毛織 ABS Starex BF-0930 M;BF-0679P M:
| Samsung Cheil Industries Starex? BF-0679P MABS, Unreinforced Scratch Resistant | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; ABS Polymer | ||
| Material Notes: |
Scratch resistant material that is used for the exterior material of flat TV
Information provided by Samsung Cheil Industries. |
||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow |
0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
ASTM D955 | ||
| Linear Mold Shrinkage, Transverse |
0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 | ||
| Melt Flow |
13 g/10 min @Load 10.0 kg, Temperature 220 °C |
13 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 116 | 116 | ASTM D785 | ||
| Tensile Strength at Break | 40.2 MPa | 5830 psi | 5 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 5 mm/min; ASTM D638 | ||
| Elongation at Break | 18 % | 18 % | 5 mm/min; ASTM D638 | ||
| Tensile Modulus | 2.45 GPa | 356 ksi | 5 mm/min; ASTM D638 | ||
| Flexural Strength | 71.6 MPa | 10400 psi | 2.8 mm/min; ASTM D790 | ||
| Flexural Modulus | 2.36 GPa | 343 ksi | 2.8 mm/min; ASTM D790 | ||
Izod Impact, Notched 
|
0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 | ||
|
0.922 J/cm @Thickness 3.17 mm |
1.73 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) |
94.0 °C @Thickness 6.40 mm |
201 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) |
85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
ASTM D648 | ||
| Vicat Softening Point | 97.0 °C | 207 °F | B/50; ISO R306 | ||
| 100 °C | 212 °F | B/120; ISO R306 | |||
| Flammability, UL94 |
HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
|||
|
De |
|||||
| Pencil Hardness | 2H | 500g, JIS K 5401 | |||
中山市沙泊塑料有限公司:主要經(jīng)營各種工程塑膠原料(新料和改性料),包括: ABS、LCP、PBT、PPS、TPE、TPU、PA6、PA66、PET、POM、PMMA、PC、PC/ABS、PC/PBT,等改性產(chǎn)品均符合SGS檢測報(bào)告。
業(yè)務(wù)部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
中山PC,沙伯基礎(chǔ)PC,德國拜耳PC,日本帝人PC、Tel:18219005688:李生;
業(yè)務(wù)部:李厚佳
Email:ppslcp@163.com
http://www.shabosl.com/
Tel:18219005688:李生
中山PC,沙伯基礎(chǔ)PC,德國拜耳PC,日本帝人PC、Tel:18219005688:李生;
Users viewing this material also viewed the following:
Samsung Cheil Industries Starex? BF-0670T MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Infino? NF-3017H PC/ABS, Unreinforced FR
Samsung Cheil Industries Starex? BF-0930 MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex? BF-0677HF MABS, Unreinforced Scratch Resistant
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對此不承擔(dān)任何保證責(zé)任。我們原則上建議您優(yōu)先選擇“塑企通”會員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請?jiān)敿?xì)核實(shí)對方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報(bào)。
簡繁切換