LCP 7130L 美國杜邦公司 物性數(shù)據(jù)
|
②原料技術(shù)數(shù)據(jù)
|
性能項目
|
試驗條件[狀態(tài)]
|
測試方法
|
測試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
物理性能
|
比重
|
黑色
|
ASTM D-792
|
1.62
|
---
|
|
泰伯摩擦
|
---
|
ASTM D-1044
|
63
|
mg
|
|
?？s率
|
流向1.6mm
|
ASTM D-955
|
-0.1
|
%
|
|
?？s率
|
流向3.2mm
|
ASTM D-955
|
0
|
%
|
|
模縮率
|
橫向1.6mm
|
ASTM D-955
|
0.9
|
%
|
|
機械性能
|
?？s率
|
橫向3.2mm
|
ASTM D-955
|
0.8
|
%
|
|
洛氏硬度
|
Scale M
|
ASTM D-785
|
63
|
---
|
|
沖擊下機械性能
|
---
|
UL 746B
|
210
|
oC
|
|
拉伸強度
|
23℃,1.6mm
|
ASTM D-638
|
173
|
MPa
|
|
拉伸強度
|
23℃,3.2mm
|
ASTM D-638
|
150
|
MPa
|
|
斷裂伸長率
|
23℃,1.6mm
|
ASTM D-638
|
1.6
|
%
|
|
斷裂伸長率
|
23℃,3.2mm
|
ASTM D-638
|
1.7
|
%
|
|
拉伸模量
|
23℃,1.6mm
|
ASTM D-638
|
19306
|
MPa
|
|
拉伸模量
|
23℃,3.2mm
|
ASTM D-638
|
18000
|
MPa
|
|
彎曲模量
|
23℃,0.8mm
|
ASTM D-790
|
18000
|
MPa
|
|
彎曲模量
|
23℃,1.6mm
|
ASTM D-790
|
14000
|
MPa
|
|
彎曲模量
|
23℃,3.2mm
|
ASTM D-790
|
13100
|
MPa
|
|
無缺口沖擊強度
|
23℃,1.6mm
|
ASTM D-4812
|
840
|
j/m
|
|
無缺口沖擊強度
|
23℃,3.2mm
|
ASTM D-4812
|
555,20%NB
|
j/m
|
|
彎曲強度
|
23℃,0.8mm
|
ASTM D-790
|
215
|
MPa
|
|
彎曲強度
|
23℃,1.6mm
|
ASTM D-790
|
192
|
MPa
|
|
彎曲強度
|
23℃,3.2mm
|
ASTM D-790
|
183
|
MPa
|
|
壓縮強度
|
3.2mm
|
ASTM D-695
|
89
|
MPa
|
|
彎曲疲勞
|
3.2mm，69MPa
|
ASTM D-671
|
2667
|
cycle
|
|
IZOD沖擊強度
|
23℃,0.8mm
|
ASTM D-256
|
400,40%NB
|
j/m
|
|
IZOD沖擊強度
|
23℃,1.6mm
|
ASTM D-256
|
170
|
j/m
|
|
IZOD沖擊強度
|
23℃,3.2mm
|
ASTM D-256
|
225
|
j/m
|
|
電氣性能
|
介電強度
|
1.6mm逐步
|
ASTM D-149
|
31
|
KV/mm
|
|
介電強度
|
23℃,1.6mm短時間
|
ASTM D-149
|
35
|
KV/mm
|
|
介電強度
|
23℃,3.2mm短時間
|
ASTM D-149
|
＞28
|
KV/mm
|
|
表面電阻率
|
---
|
ASTM D-257
|
1×1015
|
Ω
|
|
體積電阻率
|
---
|
ASTM D-257
|
1×1016
|
Ω.cm
|
|
損耗因素
|
23℃,3.2mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
|
損耗因素
|
23℃,0.8mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
|
損耗因素
|
23℃,1.6mm,1×109Hz
|
ASTM D-2520B
|
0.004
|
---
|
|
損耗因素
|
23℃,0.8mm,1×103Hz
|
ASTM D-150
|
0.013
|
---
|
|
損耗因素
|
23℃,3.2mm,1×103Hz
|
ASTM D-150
|
0.013
|
---
|
|
損耗因素
|
23℃,0.8mm,1×106Hz
|
ASTM D-150
|
0.029
|
---
|
|
損耗因素
|
23℃,3.2mm,1×106Hz
|
ASTM D-150
|
0.029
|
---
|
|
介電常數(shù)
|
23℃,0.8mm,1×103Hz
|
ASTM D-150
|
3.9
|
---
|
|
介電常數(shù)
|
23℃,3.2mm,1×103Hz
|
ASTM D-150
|
4.3
|
---
|
|
介電常數(shù)
|
23℃,0.8mm,1×106Hz
|
ASTM D-150
|
3.5
|
---
|
|
介電常數(shù)
|
23℃,3.2mm,1×106Hz
|
ASTM D-150
|
3.8
|
---
|
|
介電常數(shù)
|
23℃,0.8mm,1×109Hz
|
ASTM D-2520B
|
4.4
|
---
|
|
介電常數(shù)
|
23℃,3.2mm,1×109Hz
|
ASTM D-2520B
|
4.3
|
---
|
|
加工性能
|
熔解溫度范圍
|
℃
|
---
|
363～371
|
---
|
|
模具溫度范圍
|
℃
|
---
|
30～95
|
---
|
|
干燥時間（除濕干燥劑）
|
---
|
---
|
2
|
h
|
|
干燥溫度
|
---
|
---
|
135
|
℃
|
|
加工時水氣含量
|
---
|
---
|
＜0.01
|
%
|
|
熱 性 能
|
相關(guān)溫度指數(shù)
|
---
|
UL 746B
|
240
|
oC
|
|
熔點
|
---
|
ASTM D-3418
|
352
|
oC
|
|
導(dǎo)熱性
|
---
|
ASTM C-177
|
0.32
|
W/m k
|
|
熱變形溫度
|
---
|
ASTM D-648
|
289
|
oC
|
|
玻璃轉(zhuǎn)變溫度
|
---
|
ASTM D-3418
|
120
|
oC
|
|
外推終融溫
|
---
|
ASTM D-3418
|
360
|
oC
|
|
其它性能
|
厚度測試
|
---
|
UL 94
|
0.75
|
mm
|
|
限制氧氣指數(shù)
|
3.2mm
|
ASTM D-2863
|
39
|
%
|
|
厚度比率
|
---
|
UL 94
|
V-0
|
---
|